Customized Size PETG Plastic Sheet Coated Overlay Film With High
Temperature Resistance
1. Introduction of Customized Size PETG Plastic Sheet Coated
Overlay Film With High Temperature Resistance
PETG Coated Overlay ( PETG Coated Film) for PETG Card body production (Model: MCO-PETG) has such features as impact resistance, high temperature resistance, anti-static, abrasion, folding and high strength. It is widely used for the production of high-end credit cards, ID cards, special packaging and printing industry.
PETG is a kind of transparent amorphous co polyester.
The performance of PETG is quite different from PET and PC. PETG plate has outstanding toughness and high impact strength, its impact strength is 3-10 times more than ordinary plastic plate, and it has a wide processing range, high mechanical strength and excellent flexibility. Compared with PVC, it has high transparency, good luster and easy to print. At the same time, PETG has environmental protection advantages, and it can be recycled without polluting the environment. PETG sheet has low flammability, good fire resistance, no combustion support, low smoke emission, no harmful substances after combustion.
2. Parameters of Customized Size PETG Plastic Sheet Coated Overlay Film With High Temperature Resistance
| Item | Parameters |
| Vicat softening point (B50) | 74±2 |
| Vicat softening point (A120) | 78±2 |
| Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
| Surface Dyne (dynes/cm) | ≥38 |
| Normal thickness in mm | 0.04,0.05,0.06,0.08,0.10 |
| Density (g/cm3) | 1.20 ±0.05 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
Laminating Condition:
| Suggested Laminating Condition | Laminating Unit | Heat Laminating | Cool Laminating |
| Temp | 110~130°C | ≤25°C | |
| Time | 25min | 15 min | |
| Pressure | ≥5Mpa | ≥5Mpa |
3. Application of Customized Size PETG Plastic Sheet Coated Overlay Film With High Temperature Resistance