PVC Uncoated Overlay Film Used For Lamination With Partially / Less-printed PVC Sheets
| 1. PVC Uncoated Overlay Film Introduction |
PVC uncoated overlay MUO-G1 model is used for lamination with partially or less-printed PVC sheets . With the right lamination parameter setting , It can also realize high adhesion , no color change and deformation.
PVC Strong Coated Overlay Film with Strong initial viscous force , slow decline , yellowing resistance ,
deformating resistance after laminating .The surface is smooth , and easy to use. Mainly used for protective
film of bank card , social security card , IC card , RF card and other card with higher requirements .
Technical Parameters:
| Item | Parameters |
| Vicat softening point | 72±2 ℃ |
| Heating Shrinkage ratio | ≤ 10 % |
| Tensile Strength | ≥ 40 MPa |
| Normal thickness in mm | 0.04 , 0.05,0.06,0.08,0.10 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
| 2. PVC Uncoated Overlay Film Specification |
| Item | Unit | Value | |
| Density | g/cm3 | 1.26 ±0.04 | |
| Tensile Strength | Horizontal | MPa | ≥35 |
| Vertical | ≥40 | ||
| Vicat 5kg | ℃ | 72±2 | |
1. Size : in reel or sheet , A4 , A3 or as per customer
requirements
2. Normal thickness : 0.04,0.05,0.06,0.08,0.10mm
3. Color : transparent with one-side glue coating
4. Package method : by reel or 500 sheets per bag / 4-8 bags per paper carton , or as per customer requirements
5. Storage condition: Sealed , moisture-proof , room temperature under 40℃ , Keep it horizontally, avoid heavy pressing and direct sunlight .
* Customer design can be accept.
3. Applications of PVC Uncoated Overlay Film
| 4. Packing of PVC Strong Coated Overlay Film |