Heat-resistant PETG Plastic Sheet /PETG Card Base for Passport and ID cards Making
1.Heat-resistant PETG Plastic Sheet /PETG Card Base- Introduction
Heat-resistant PETG Plastic Sheet /PETG Card Base is widely used in card base production. It has such features as impact resistance, high temperature resistance, anti-static, abrasion, folding and high strength. It is widely used for the production of high-end credit cards, ID cards and passport, etc.
PETG is a kind of transparent amorphous copolyester.
Features:
1).Excellent strength and wear-resisting
2).High temperature and low temperate resistance;
3).Perfect application for laser Engraving
4).Environment-friendly material
5).Longer service life
| Item | PETG Core Sheet |
| Color | White |
| Thickness Range(mm) | 0.1-0.76 |
| Vicat point ℃ | 78-80 ± 2 |
| Tensile strength | ≥50 Mpa |
| Surface | Both sides matt |
| Density | 1.3 ± 0.05 |
| Transparency | ≤5 |
| Heat shrink | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
2.Heat-resistant PETG Plastic Sheet /PETG Card Base- Parameters
The performance of PETG is quite different from PET and PC. PETG plate has outstanding toughness and high impact strength, its impact strength is 3-10 times more than ordinary plastic plate, and it has a wide processing range, high mechanical strength and excellent flexibility. Compared with PVC, it has high transparency, good luster and easy to print. At the same time, PETG has environmental protection advantages, and it can be recycled without polluting the environment. PETG sheet has low flammability, good fire resistance, no combustion support, low smoke emission, no harmful substances after combustion.
Technical Parameters:
| Item | Parameters |
| Vicat softening point (B50) | 78±2 |
| Vicat softening point (A120) | 80±2 |
| Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
| Surface Dyne (dynes/cm) | ≥38 |
| Normal thickness in mm | 0.10-0.76 |
| Density (g/cm3) | 1.30 ±0.05 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
3.Heat-resistant PETG Plastic Sheet /PETG Card Base - Application
Used for the protecting layer of various kinds of PETG material cards.
Card-making method:
1). Print the patterns directly to the material
2). Laminate with overlay
3). Punching
4). Other art-work
| Product model | Product name | Thickness Range mm | Color | Vicat ℃ | dynes/cm | Apparent density g/cm3 | Peel strength N/cm | Main application |
| PETG | PETG core | 0.1-0.76 | White
| 78-80 | ≥38 | 1.3+/-0.05 | / | It is used for national ID cards and other high grade cards.It is capable of achieving laser ablation, sunken cord, leveling up, printed layer,and has resistance to high temperature, high strength and environmental protection. |
| Item | Unit | Value | |
| Density | g/cm3 | 1.30 ±0.05 | |
| Tensile Strength | Horizontal | MPa | ≥50 |
| Vertical | ≥50 | ||
| Vicat | ℃ | 78-80 | |
| Surface Dyne | dynes/cm | ≥38 | |
| Thickness range | mm | 0.1-0.76mm | |
4.Heat-resistant PETG Plastic Sheet /PETG Card Base - Packing
Characteristic:
1.Good lamination properties
2.Good impact resistance
3.Good chemical resistance
4.Excellent printability with either offset or screen printing
5.Laminating Temp 120 degrees Celcius-130 degrees Celcius (lab conditions)