ASTM A312 UNS S30815 (253MA) Pipe DN15-DN1200 SCH40S
| Product Name | ASTM A312 UNS S30815 (253MA) Pipe |
| Standard | ASME/ANSI B16.5/16.36/16.47A/16.47B, MSS S44, ISO70051, JISB2220, BS1560-3.1, API7S-15, API7S-43, API605, EN1092 |
| Type | 1.4835 (UNS S30815 – 253MA – SS2368)Pipe |
| Materials | Stainless steel:ASTM/ASMES/A182 F304 | F304L |F304H | F316 | F316L | F321 | F321H | F347|316Ti | 309S |310S | 405 |409|410 | 410S | 416 | 420 | 430 | 630 | 660 | 254SMO | 253MA | 353MA N06625 | N08800 | N08810 | N08825 | N10276 | N10665 | N10675 | Incoloy 800 | Incoloy 800H | Incoloy 800HT | Incoloy 825 | Incoloy 901 | Incoloy 925 | Incoloy 926, Inconel 600 | Inconel 601 | Inconel 625 | Inconel 706 | Inconel 718 | Inconel X-750, Monel 400 | Monel 401 | Monel R 405 | Monel K 500 S32760 Hastelloy C-22 | Hastelloy C-276 | Hastelloy X |Hastelloy G | Hastelloy G3 S32304 |
| Marking | Supply Logo + Standard + Size(mm) + HEAT NO +or as your requirement |
| Test | Chemical Component Analysis, Mechanical Properties, Metallurgical Analysis, Impact Testing, Hardness testing , Ferrite Testing, Intergranular corrosion testing, X-ray Inspection (RT), PMI, PT, UT, HIC & SSC test, etc. or as your requirment |
| Certificates | API, ISO, SGS, BV, CE, PED, KOC, CCRC, PDO, CH2M HILL and etc. |
| Applications | Ø EN 1.4835 has a good weldability and can be welded using the following methods: 1. Shielded metal arc welding (SMAW) 2. Gas tungsten arc welding, GTAW (TIG) 3. Plasma arc welding (PAW) 4. Gas metal arc GMAW (MIG) 5. Submerged-arc welding (SAW) Ø Typical application areas for 1.4835: 1. Ovens 2. Construction 3. Building 4. As details at high temperature |
| Advantages | 1.Corrosion Resistance 2.Heat Resistance 3.Heat Treatment 4.Welding 5.Machining |
Material Description
1.4835 (UNS S30815 – 253MA – SS2368)
253MA Stainless Steel is Rare Earth Metals (REM) and lean austenitic heat resistant alloy with high strength and outstanding oxidation resistance. 253 MA maintains its heat resistant properties by advanced control of micro alloy additions. The use of rare earth metals in combination with silicon gives superior oxidation resistance up to 2000°F. Nitrogen, carbon and a dispersion of rare earth and alkali metal oxides combine to provide creep rupture strength comparable to the nickel base alloys. A wide variety of components requiring high strength at elevated temperature such as heat exchanger, kilns, stack dampers and oven components are common applications for 253 MA.
253MA is a grade combining excellent service properties at high temperature with ease of fabrication. It resists oxidation at temperatures up to 1150°C and can provide superior service to Grade 310 in carbon, nitrogen and sulphur containing atmospheres. Another proprietary designation covering this grade is 2111HTR.
253MA contains fairly low nickel content, which gives it some advantage in reducing sulphide atmospheres when compared to high nickel alloys and to Grade 310. The inclusion of high silicon, nitrogen and cerium contents gives the steel good oxide stability, high elevated temperature strength and excellent resistance to sigma phase precipitation.
The austenitic structure gives this grade excellent toughness, even down to cryogenic temperatures. These properties are specified for flat rolled product (stainless steel plate, sheet and coil) as Grade S30815 in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as pipe and bar in their respective specifications.
Function
The steel grade 1.4835 ( also called UNS S30815, 253MA and SS2368) is an austenitic stainless high temperature steel with good resistance to oxidation. The steel has been designed to be used at temperatures over 550°C, the most suitable temperature range is 850-1100°C. The steel suits for production of details with good resistance to temperature corrosion and relatively high strength at elevated temperatures. It also has good creep strength properties. 1.4835 is not magnetic but can be slightly magnetic after cold working or welding.
Good formability and weldability
1.4835 has a good weldability and can be welded with shielded metal
arc welding, gas tungsten arc welding, plasma arc welding and
submerged-arc welding. You shall use low heat input and use filler
metals of type EN 1.4835 when you weld. The steel can be both
cold and hot formed but it can only be hardened by cold
working. The steel has high hardness and at machining you need to
follow cutting recommendations.
| Grade | C | Mn | Si | P | S | Cr | Ni | N | Ce | |
| 253MA | min. max. | 0.05 0.10 | 0.8 | 1.10 2.00 | 0.04 | 0.03 | 20.0 22.0 | 10.0 12.0 | 0.14 0.20 | 0.03 0.08 |
Chemical Composition ranges for 253MA grade stainless steel
Mechanical properties of 253MA grade stainless steel
| Grade | Tensile Strength | Yield Strength | Elongation (% in 50mm) min | Hardness | |
| (MPa) min | 0.2% Proof (MPa) min | Rockwell B | Brinell (HB) max | ||
| (HR B) max | |||||
| 253MA | 600 | 310 | 40 | 95 | 217 |
Physical properties of 253MA grade stainless steel
| Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion (mm/m/°C) | Thermal Conductivity (W/m.K) | Specific Heat | Electrical Resistivity (nW.m) | |||
| 0-100°C | 0-600°C | 0-1000°C | at 20°C | at 1000°C | 0-100°C (J/kg.K) | ||||
| 253MA | 7800 | 200 | 17 | 18.5 | 19.5 | 15 | 29 | 500 | 850 |
Grade specifications Comparison for 253MA grade stainless steel
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| 253MA | S30815 | - | - | 1.4835 | X9CrNiSiNCe21-11-2 | 2368 | - |
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted. | |||||||
Possible alternative grades to 253MA grade stainless steel
| Grade | Why it might be chosen instead of 253MA |
| 310 | Carburising atmospheres require a higher nickel content |
| 304H | Lower cost alternative, provided the operating temperature is below about 800°C |
| Nickel Alloys | Carburising atmospheres or temperatures above the 1100 - 1150°C maximum of 253MA. |
FAQ
Q: Are you trading company or manufacturer ?
A: We are manufacturer ,You can see the Alibaba certification.
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is
15-20 days if the goods are not in stock, it is according to
quantity.
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but need pay the
cost of freight.
Q: What is your terms of payment ?
A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50%
T/T in advance ,balance before shippment.