BeCu Rod TD04&TH04 C17300 Beryllium Copper Rod 2mm~10mm For Spring Contact Test Probes &
BeCu Rod TD04&TH04 C17300 Beryllium Copper Rod 2mm~10mm for Spring Contact Test Probes
Product Description:
Name: High Strength Beryllium Copper Bar
Grade: C17300
End Product Form: Rods/ Bars
Standard: ASTM B196, QQ-C-530
State of product: A(TB00),H(TD04),AT(TF00),HT(TH04)
Processing: Seamless / Welding
Feature: With high strength and high conductivity
Package: Pack in coil+waterproofing winding film+Drier+Wooden Case
Specification: Length: according customers' requirement
CUBERYLLIUM® manufactures copper beryllium in several distinct compositions. These fall into two categories: alloys selected for high strength (Alloys 172,173,170) and alloys selected for high conductivity (Alloys 751,750,741). And Gost standard QBe2,QBe1.9Ti for Russia Market. Also Supply Master alloy : CuBeryllium-200; CuBeryllium-275);CuBeryllium-350 and Cuberyllium-400 to global factory.
Beryllium copper has its reasonable share of common names. You will listen referred to as BeCu, Copper Beryllium, Beryllium Bronze, and Spring Copper. Anytime you hear those terms, they're in reference to Beryllium Copper. Beryllium round bars are accessible as high strength and high conductivity alloys.
CUBERYLLIUM ®-173 also named -C17300 (CDA 173) offers the strength properties of C17300 with the added benefit of being “free machining”. C17300 rod and wire contain a small amount of lead to provide an alloy tailored for automatic machining operations. Lead promotes formation of finely divided chips thus extending cutting tool life.
Chemical Composition of High Strength Beryllium Copper Alloys C17300:
| CUBERYLLIUM® Brand | UNS-Number | Beryllium | Cobalt + Nickel | +Cobalt + Nickel + Iron | Pb | Copper |
| Cuberyllium-C173 | C17300 | 1.80-2.00 | 0.20 min | 0.6 max | 0.2～0.6 | Balance |
Note: Copper plus additions equal 99.5% minimum.
Typical Physical Properties of High Strength Beryllium Copper Alloys C17300:
Density: 8.36g/cm3
Density before age hardening: 8.25g/cm3
Melting Range: 870~980℃
Elastic Modulus((kg/mm2 (103)): 13.4
Thermal Expansion Coefficient(20 °C to 200 °C m/m/°C): 17 x 10 -6
Thermal Conductivity(cal/(cm-s-°C)): 0.25
Mechanical and Electrical Properties of High Strength Beryllium Copper Bar C17300:
| Temper(*) | Diameter | Heat Treatment | Tensile Strength ksi | Elogation Percent (Min) | Electrical Conductivity Percent IACS | Hardness Rockwell B or C Scale |
|---|---|---|---|---|---|---|
| A(TB00) | ALL SIZE | / | 400~600 | 30 | 15~19 | B45~85 |
H(TD04) | 5~10 | / | 660~900 | 5 | 15~19 | ＞B88 |
| ＞10~25 | / | 620~860 | 5 | 15~19 | ||
| ＞25 | / | 590~830 | 5 | 15~19 | ||
| AT(TF00) | ALL SIZE | 3 hr 320°C | 1100~1380 | 2 | 22~28 | C35~42 |
| HT(TH04) | 5~10 | 2 hr 320°C | 1200~1550 | 1 | 22~28 | C37~45 |
| ＞10~25 | 1150~1520 | 1 | 22~28 | C36~44 | ||
| ＞25 | 1120~1480 | 1 | 22~28 | C35~44 |
Product Photo:
High Strength Beryllium Copper Alloys C17300 International Specification:
Rods/Bars/Tubes: ASTM B196, QQ-C-530
Wires: ASTM B197, QQ-C-530
European Standards: CuBe2Pb, Alloy M25, UNS.C17300, DIN.2.1248, CW102C to EN
Note:
ASTM: American Society for Testing and Materials
SAE: Society of Automotive Engineers
AMS: Aerospace Materials Specification(Published by SEA)
RWMA: Resistance Welder Manufacturers' Association
Note: Unless otherwise specified, material will be produced by ASTM.
Typical Applications for High Strength Beryllium Copper Alloys C17300:
Electrical Industry: Switch Parts, Relay parts, RF Coaxial
Connector, Contact Bridges, Electrical Connectors, Fuse Clips,
Electrical Motor Components, Navigational Instruments, Electrical
Switch and Relay Blades.
Industrial: Bushings, Welding Equipment, Non-Sparking Safety Tools,
Shafts, Springs, Rolling Mill Parts, Spline Shafts, Pump
Parts, Valves, Bourdon Tubes, Bellows, Electrochemical Springs,
Flexible Metal Hos
Key Technology of Beryllium Copper(Heat treatment)
Age Hardening
Age hardening significantly enhances the material’s strength. This reaction is generally carried out at temperatures between 260°C and 540°C depending on alloy and desired characteristics. This cycle causes the dissolved beryllium to precipitate as a beryllium rich (gamma) phase in the matrix and at the grain boundaries. It is the formation of this precipitate which causes the large increase in material strength. The level of mechanical properties attained is determined by the temperature and time at temperature. It should be recognized that beryllium copper has no room temperature aging characteristics.
FAQ:
Q1:What’s the advantages the Beryllium Copper of CUBERYLLIUM®?
A1: 1: The Biggest Coil weight could be reach 1200kg/Coil.
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q2: How about your payment terms?
A2: Generally, 30% as deposit by T/T, then 70% should be paid
before the delivery.
Q3: Why you melting by Vacuum semi-Continuous Furnace?
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.