Feature:
Item | Test standard and method | Test | |
Appearance | Color uniform, loose without blocking, dry coating liquidity 120—140mm | visual | |
color | As customer required | Chromatic meter | |
Adhesion | GB/T9286-1998 | ISO2409 | 0 class |
Impact resistance | GB/T1732-1993 | ISO6272 | 50kg.cm |
flexibility | GB/6742-1986 | ISO1519 | 3mm |
Cupping test | GB/T9753-1993 | ISO1520 | 8mm |
Pencil hardness | GB/T6739-1996 | ASTM/D3363 | 1H-2H |
Salt spray testing | GB/T1771-1991 | ISO7253 | > 1000hour |
Product Details | |
Product Name | RAL 9005 Black Powder Coating |
Product Code No. | WAB |
Color | Black |
Gloss Level | N/A |
Surface Finish | Smooth |
Powder Property | |
Appearance | Fine powder |
Particle Size | Average 32-42μm |
Specific Gravity | 1.3-1.6g/cm3 |
Coverage | 7-8 square meter per Kg at 80μm film thickness |
Application Recommendation | |
Applicatoin | Corona |
Application Voltage | 60-90 KV |
Gun to Component Distance | 15-30 CM |
Film Thickness | 80-90μm |
Curing Temperature | 190℃(Object temperature) for 15 minutes |
Powder Coated Film Mechanical Properties | |
Adhesion | Cross-cut (2mm), no loss of adhesion |
Impact Resistance | Direct & Indirect 50kg/cm |
Pencil Hardness | 2H |
Flexibility | 6mm Mandrel |
Bending Test | 3mm |
Powder Coated Film Chemical Resistance | |
Salt Spray Test | 5% NaCl Solution for 500 hours - No change |
Acid Resistance | 5% HCL for 48 hours dip test - No change |
Alkali Resistance | 5% NaOH for 48 hours dip test - No change |
Surface Preparation | |
All surfaces shall be degreased and pre-treated for optimal performance before application | |
Aluminium | Yellow chromate or green chromate/phosphate |
Ferrous metals | Zinc phosphate or Iron phosphate |
Zinc coated metals | Zinc phosphate or choromate conversion |
Storage Stability | |
Store in ventilated, dry, clean room, temperature < 25℃ | |
Relative humidity 50-65% | |
Away from direct sunlight, fire, heat | |
For best performance, use within 6 months |