High Quality Mill finished and Bule/Gold Hydrophilic
Aluminium Foil 8011 8079 0.15mm to 0.35 mm for the Fin and Air
Conditioner
Aluminium fin foil :
Mill finsihed and hydrophilic aluminium foil finstock is widely
used in household and Industry air conditioner ,refrigerrator ,cold
equipment and vehicle air ec
1. alloy :1100,1200,1145,8011,8006
2. temper :h12,h14,h16,h18 ,h22,O
3. thicknes:0.15mm to 0.45mm
4. widht :150mm to 600mm
our company ajust the alloy and develop DS-1,DS-2,DS-3 which are
good in mechanical and hydrophilic capability on the basis of
1100,1200,1145,8006 with all kinds of size !
Place of Origin | Zhejiang, China (Mainland) |
Brand Name | Shuanglin Jiate |
Model Number | 8006 8011 |
Grade | 8000 Series |
Thickness | 0.15mm --0.45mmm |
Width | 150mm --600mm |
Application | hydrophilic aluminium finstock |
Surface Treatment | Coated |
Hardness | 30 |
Alloy Or Not | Non-alloy |
Al (Min) | 99.5 |
Yield (≥ MPa) | 7o |
Temper | O - H112 |
Ultimate Strength (≥ MPa) | 100 |
Elongation (≥ %) | 10 |
Product Brief Introduction:
(Ⅰ) Aluminum Coil/Foil Used for Air Conditioner and Others
(packing.Cable and pipe)
Alloy | Temper | Physical Properties under Room Temperature | ||
U.T.S 6 b ,Mpa | Elongation e% | Cupping Value IE,mm | ||
1100 1235 8079 | O | 80～110 | ≥20 | ≥6.0 |
H22 | 100～135 | ≥16 | ≥5.5 | |
H24 | 115～145 | ≥12 | ≥5.0 | |
H26 | 125～160 | ≥8 | ≥4.0 | |
H18 | ≥160 | ≥1 | -- | |
Mark: Special specifications you need can be negotiated and marked in the contract | ||||
Thickness & Tolerance mm | Width & Tolerance mm | Core I. D. mm | Max. Roll O. D. mm | Core Material |
0.009～0.02 | 100～1100 ±0.5 | Φ75,Φ150,Φ200 | Φ≤1400 | Paper, Aluminum, Steel |
◆The Coat Properties of Hydrophilic Coated Foil:
No. | Item Index | Technology Index | |
1 | Film Thickness | 1.0-2.0μm(Average Thickness for Single Face) | |
2 | Hydrophilicity | Initial Contact Angle | Initial Contact Angle≤10° |
Persistent Contact Angle | Persistent Contact Angle≤20° | ||
3 | Adhesive Power | Cupping Testing(5mm pressed by): no Flake | |
4 | Corrosion Resistance | Salt Spray Testing(72 hours) | |
5 | Alkali Resistance | Soaked in 20℃,20%NaOH for 3 minutes | |
6 | Solvent Resistance | Weight Loss of Sample≤1% | |
7 | Stability | under 200℃ for 5 min, the color will not change | |
8 | Oil Resistance | Soaked in volatile oil for 24 hours without bubbling | |
9 | Coat Odor | No Peculiar Odor | |
10 | Abrasion against Mould | The Same as Common Aluminum Foil | |