Industrial Furnace Fecral Electric Resistance Heating Wire Industrial Furnace for Electric Resistance Heating Wire
Product Description
Model Number:Resistance heating 0Cr25AL5 wire
Application:Home appliances,industrial furnaces,making electric
heating element
Shape:Wire,strip,ribbon etc
Material:Iron-Chromium-Aluminium Alloy
Chemical Composition:Ferro Chrome Aluminium
Ferro Chrome Aluminium:Resistance heating 0Cr25AL5 wire
Standard:AISI,ASTM,DIN,GB etc
Standard:GB/ASTM/AISI/ASME/JIS/DIN etc
Type:Wire /strip /ribbon etc
Certificate:ISO 9001&ROHS&TUV
Conductor Material:Ferro Chrome Aluminium alloy
Surface:Bright and smooth
Surface Treatment:Polished and oxidation
Property:Resistance heating 0Cr25AL5 wire
Feature:Good form stability
FeCrAl wire strip includes: OCr13Al4,OCr19Al3,OCr21Al4,OCr20Al5,OCr25Al5,OCr21Al6,OCr21Al6Nb,OCr27Al7Mo2.
Nickel chrome wire Strip Bar includes: Cr25Ni20,Cr20Ni35,Cr15Ni60,Cr20Ni80.
Copper Nickel wire Strip includes:
CuNi1,CuNi2,CuNi5,CuNi8,CuNi10,CuNi14,CuNi19,CuNi23,CuNi30,CuNi34,CuNi44.
Constantan wire includes: 6J40,4J42,4J32.
Manganin wire:6J8,6J12,6J13.
Main grades and properties
Grades Properties | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
Chemical composition % | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
Fe | Balance | Balance | Balance | Balance | Balance | Balance | Balance | |
Other | Nb 0.5 | Mo1.8-2.2 | ||||||
Highest service temperature °C | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
ResistivityμΩ.M,20°C | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Density (g/cm3 ) | 7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
Thermal conductivity KJ/m.H.°C | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coefficient of linear extensibility Α×10-6/°C | 15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
Melting point °C | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Tensile Mpa | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Elongation % | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Reduction % | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Hardness H.B. | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Microstructure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |