Soft Magnetic Alloys Strip 1J50/ Ni 50 Ni-Fe soft magnetic alloy
strip
Mainly used in two areas for energy conversion and information
processing
In the power industry, mainly in the high magnetic field has a high
magnetic induction and low core loss of the alloy. In the
electronics industry, mainly at low or medium alloy having a high
magnetic permeability and low coercive force. At high frequencies
shall be made on a thin strip or alloy higher resistivity. Usually
with sheet or strip.
Soft magnetic materials in exchange for use, due to the alternating
magnetic eddy currents are induced inside the material, resulting
in the loss, the smaller the resistance of the alloy, the greater
the thickness, the higher the frequency of the alternating magnetic
field, eddy current losses greater, magnetic reduce more. For this,
the material must be made thinner sheet (tape), and the surface
coated with an insulating layer, or the use of certain methods to
the surface to form an oxide insulating layer, such alloys commonly
used magnesium oxide electrophoresis coating.
Iron-nickel alloy mostly in the alternating magnetic field use,
mainly for yoke iron, relay, Small Power Transformers and
Magnetically shielded.
Shanghai Tankii Alloy Material Co., Ltd. Focus on the production of
resistance alloy(nichrome Alloy, FeCrAl Alloy, copper nickel alloy,
thermocouple wire, precision alloy and thermal spray alloy in the
form of wire, sheet, tape, strip, rod and plate. We've already got
ISO9001 quality system certificate and approval of ISO14001
environmental protection system. We own a complete set of advanced
production flow of refining, cold reduction, drawing and heat
treating etc. We also proudly have independent R&D capacity.
Shanghai Tankii Alloy Material Co., Ltd has accumulated lots of
experiences over 35 years in this field. During these years, more
than 60 management elites and high science and technology talents
were employed. They participated in every walk of the company life,
which make our company keep blooming and invincible in the
competitive market. Based on the principle of "first quality,
sincere service", our managing ideology is pursuing technology
innovation and creating the top brand in the alloy field. We
persist in Quality - the foundation of the survival. It is our
forever ideology to serve you with full heart and soul. We
committed to provide customers all over the world with
high-quality, competitive products and perfect service.
Our products, such us nichrome alloy, precision alloy, thermocouple
wire, fecral alloy, copper nickel alloy, thermal spray alloy have
been exported to over 60 countries in the world. We are willing to
establish strong and long-time partnership with our customers. Most
complete range of products dedicated to Resistance, Thermocouple
and Furnace manufacturers Quality with end to end production
control Technical support and Customer Service.
The following are details of our products 1J50:
| Grade | C | P | S | Cu | Mn | Si | Ni | Cr | Fe |
| 1J50 | 0.03 | 0.020 | 0.020 | 0.20 | 0.30~0.60 | 0.15~0.30 | 49.0~51.0 | - | B |
Mechanical property
| Yield strength | Tensile Strength | Elongation |
| Mpa | Mpa | % |
| 685 | 780 | 3~35 |
Physical property
| Density (g/cm3) | 8.2 |
| Resistivity under 20℃(Ωmm2/m) | 0.45 |
| Linear expansion coefficient (20℃-200℃) X10-6/℃ | 9.2 |
| Saturation magnetostrictive coefficient, λθ/ 10-6 | 25 |
| Curie point, Tc/ ℃ | 500 |
Magnetic property
| 1J50 | Initial magnetic permeability | Max.magnetic permeability | Coercive force | Saturation induction intensity |
| Cold rolled strip/sheet material thickness, mm | μ0.08/ (mH/m) | μm/ (mH/m) | Hc/ (A/m) | Bs/T |
| ≥ | ≤ | |||
| 0.05 mm | 2.5 | 35 | 20 | 1.5 |
| 0.1~0.19 mm | 3.8 | 43.8 | 12 | |
| 0.2~0.34 mm | 4.4 | 56.3 | 10.4 | |
| 0.35~1.0 mm | 5 | 65 | 8.8 | |
| 1.1~2.5 mm | 3.8 | 44 | 12 | |
| Bar | ||||
| 8-100 mm | 3.1 | 25 | 24 | 1.5 |
Heat treatment process
| Annealing medium | Dry hydrogen ( dew point is no more than -40℃) or vacuum, with a residual pressure of no more than 0.1Pa |
| Heating temperature and speed | 1100~1150℃ |
| Heat preservation (h) | 3~6 |
| Cooling speed | Be cooled to 600℃ at a speed of 100 ~ 200 ℃/ h, then be quickly cooled to 300℃, discharging from the furnace. |