5 mm 0Cr27Al7Mo2 Fecral Alloy Wire Oxidated Colour for Industrial Furnace Heating
FeCrAl alloy has the characteristic of high resistivity,low temperature resistance coefficient,high operating temperature,good anti-oxidation and anti-corrosion under high temperature.
It is widely used in industrial furnace, household appliances, industry furnace, metallurgy, machinery, aircraft, automotive, military and other industries producing heating elements and resistance elements.
FeCrAl alloy series: OCr15Al5,1Cr13Al4, 0Cr21Al4, 0Cr21Al6, 0Cr23Al5, 0Cr25Al5, 0Cr21Al6Nb,0Cr27Al7Mo2, and etc.
The alloy's high resistivity and extremely low electro-motive force
(EMF) versus copper are highly desired properties in precision
resistance wire. It also possesses high tensile strength, high
resistance to corrosion and is non-magnetic.
The temperature coefficient of resistance of this material is very
closely controlled by the addition of aluminum, manganese and
silicon combined with critical processing controls.
FeCrAl alloy is supplied in the annealed and heat treated condition
to ± 5 ppm in the temperature range of -67°F to 221°F (-55°C to
105°C). This results in very stable resistance.
Although FeCrAl alloy is the only high-resistance,
low-TCR alloy on which extensive stability tests have been
conducted, EVANOHM alloy S is heat treated in the same manner and
is believed to have equal stability because its properties are
produced by the same short range ordering as FeCrAl alloy.
Size dimension range:
Wire: 0.01-10mm
Ribbon: 0.05*0.2-2.0*6.0mm
Strip: 0.05*5.0-5.0*250mm
Bar:10-50mm
| Chemical Composition and Main Property of Fe-Cr-Al Resistance Alloy | ||||||||
| Properties Grade | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical Composition (%) | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max Continuous Service Temperature(oC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resisivity 20oC (Ωmm2/m) | 1.25 ±0.08 | 1.42 ±0.06 | 1.42 ±0.07 | 1.35 ±0.07 | 1.23 ±0.07 | 1.45 ±0.07 | 1.53 ±0.07 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal Conductivity | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| (KJ/m@h@oC) | ||||||||
| Coefficient of Thermal Expansion(α×10-6/oC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Approximate Melting Point( oC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile Strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Section Variation | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Shrink Rate (%) | ||||||||
| Repeatedly Bend Frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness (H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Continuous Service Time | no | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic Structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic Property | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |