0Cr21Al4 FeCrAl Alloy Electric Wire/ Coil with Dia 5mm for Heating Equipment
Product Description:
With the characteristics of high resistance, low coefficient of
electric resistance, High operating temperature, good corrosion
resistance under high temperature.
It is mainly used in electric locomotive, diesel locomotive, metro
vehicle and high Speed moving car etc
brake system brake resistor, electric ceramic cooktop, industrial furnace.
Feature:
With long service life.Heating up fast.High thermal
efficiency.Temperature uniformity. Can use vertically. When being
used in the rated voltage,there is no volatile matter.It i the ne
environmental protection electric heating wire.And an alternative
to the costly nichrome wire.Can be customized according to customer
requirements
Usage:
It is widely used in industrial furnace, household electrical
appliances, infrared heater, etc.
The key properties:
1.The thickness of surface insulation resistance to oxidation
layer: 5-15 μ m.
2. Insulation resistance: multimeter detection infinity.
3.The voltage-endurance of insulating single layer is greater than
the alternating voltage 60 ν without breakdown.
4. The use of voltage: 6-380 ν.
5. Using temperature: Maximum1200 ºC
6. Service life: not less than 6000 hours.
7.Thermal shock performance: Electric heating element can withstand
the cold and hot impact 600-6000 times without deformation.
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | -- | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| continuous service time(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |