Product Overview of Ni60Cr23:
TANKII Brand Inconel601 alloy have excellent oxidation resistance at high temperature, good
carbonization resistance, good resistance to oxidation sulfur
atmosphere, and has good mechanical properties at room and high
temperature as good resistance to stress corrosion cracking
performance due to control the carbon content and grain size,
Inconel 601 had a higher creep rupture strength, therefore it is
recommended to use in the field of above 500 ºC.
You can find below Characters of Ni60Cr23:
(1) Have excellent oxidation resistance at high temperature;
(2) Good carbonization resistance;
(3) Can be a very good resistance to oxidation sulfur atmosphere;
(4) Has good mechanical properties at room and high temperature;
(5) Good resistance to stress corrosion cracking performance due to
control the carbon content and grain size, 601 has high creep
rupture strength, therefore it is recommended to use in the field
of above 500 ºC;
Chemical Compositon of Ni60Cr23 Wt.%:
| Inconel 601 (UNS N06601/W.Nr.2.4851) | ||||||||||||||
| % | Ni | Cr | Fe | C | Mn | Si | Cu | Al | P | S | ||||
| Min | 58 | 21 | ||||||||||||
| Max | 63 | 25 | Bal. | 0.1 | 1.5 | 0.5 | 1 | 1.7 | 0.02 | 0.015 | ||||
Inconel 601's Min Value of Mechanical Properties at normal
temperature:
| Typical Mechanical Properties | Tensile Srength Rm N/mm2 | Yield Strength Rp0.2N/mm2 | Elongation A5 % | Hardness HB |
| annealed treatment | 650 | 300 | 30 | - |
| solution treatment | 600 | 240 | 30 | 220 |
Chemical Composition and Main Properties of Nichrome | ||||||
| Properties Grade | NiCr 80/20 | NiCr 70/30 | NiCr 60/15 | NiCr 35/20 | NiCr 30/20 | |
| Main Chemical Composition | Ni | Balance | Balance | 55.0-61.0 | 34.0-37.0 | 30.0-34.0 |
| Cr | 20.0-23.0 | 28.0-31.0 | 15.0-18.0 | 18.0-21.0 | 18.0-21.0 | |
| Fe | ≤ 1.0 | ≤ 1.0 | Balance | Balance | Balance | |
| Max Continuous Service Temperature(oC) | 1200 | 1250 | 1150 | 1100 | 1100 | |
| Resisivity 20oC (Ω mm2/m) | 1.09 | 1.18 | 1.12 | 1.04 | 1.04 | |
| Density (g/cm3) | 8.4 | 8.1 | 8.2 | 7.9 | 7.9 | |
| Thermal Conductivity(KJ/m@ h@ oC) | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
| Coefficient of Thermal Expansion(α × 10-6/oC) | 18 | 17 | 17 | 19 | 19 | |
| Melting Point( oC) | 1400 | 1380 | 1390 | 1390 | 1390 | |
| Elongation(%) | > 20 | > 20 | > 20 | > 20 | > 20 | |
| Micrographic Structure | austenite | austenite | austenite | austenite | austenite | |
| Magnetic Property | nonmagnetic | nonmagnetic | nonmagnetic | Weak magnetic | Weak ma | |
More detail information, please feel free contact us!