Cr15ni60 Nicrc Nichrome Resistance Wire Strip Used For Resistors
NiCr60/15
Specifications
1. Pass: ISO9001 certification
2. fine after-sale services
3. small order accepted
4. samples available
5. short delivery time
1. Introduction to products
Nickel-chromium, nickel-chromium alloy with high and stable resistance, corrosion resistance, surface oxidation resistance is good, a better under high temperature and seismic strength, good ductility, good workability and weldability.
2. Products and services
1.Pass: ISO9001 certification;
2.fine after-sale services;
3.small order accepted;
4.samples available;
3.Application
Our Products widely apply to chemical industry, metallurgy mechanism, glass industry, ceramic industry, home appliance area and so on.
4.size
wires:0.018-10mm Ribbons:0.05*0.2-2.0*6.0mm
Strips:0.5*5.0-5.0*250mm Bars:D10-100mm
Chemical Content, %
C | P | S | Mn | Si | Cr | Ni | Al | Fe | Other |
Max | |||||||||
0.08 | 0.02 | 0.015 | 0.60 | 0.75~1.60 | 15.0-18.0 | 55-61 | Max 0.50 | Bal | - |
Mechanical Properties
Max Continuous Service Temperature: Resisivity ( 20℃)/Ω·m::
Density: Thermal Conductivity: Coefficient of Thermal Expansion: Melting Point: Elongation: Micrographic Structure: Magnetic Property: | 1150℃ 1.12 +/-0.05 (Dia: <0.5mm) 1.15+/-0.05 (Dia: ≥0.50 mm) 8.2 g/cm3 45.2 KJ/m·h·℃ 17×10-6/℃ (20℃~1000℃) 1390℃ Min 20% Austenite nonmagnetic |
Temperature Factor of Electrical Resistivity
20℃ | 100℃ | 200℃ | 300℃ | 400℃ | 500℃ | 600℃ |
1 | 1.011 | 1.024 | 1.038 | 1.052 | 1.064 | 1.069 |
| ||||||
700℃ | 800℃ | 900℃ | 1000℃ | 1100℃ | 1200℃ | 1300℃ |
1.073 | 1.0278 | 1.088 | 1.095 | 1.109 | - | - |
Our Nichrome alloy are in the form of wire, ribbon, strip, coil.
Delivery conditions are:
Our major product line:
l Electric resistance alloy materials in wire, strip, tube, and bar form.
l Furnace products and heating systems: