project | Test Results | |
A Component | B Component | after mixing | |
Color and Viscosity | white paste | black paste | Black non-flowing paste | |
proportion | 1.35 | 1.03 | 1.33 | |
Main agent, catalyst by weight 12:1(Volume ratio 9:1)after mixing |
Construction time(ºC,50%RH) | | | 20-40minute | |
Dry time(ºC,50%RH) | | | 80-100minute | |
Corrosive | | | none | |
After curing - at temperature25ºC,7 days after construction at 50% relative humidity |
project | result | |
Hardness (Shore A) | 40 | |
12.5%Tensile modulus at elongationMPa | 0.17 | |
ultimate tensile strengthMPa | 0.93 | |
Ultimate Elongation (Break) | 150% | |